PEI ProPolymers PEI 1010 PROPOLYMERS USA

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap		ASTM D256	32 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	5.00 kJ/m²
Suspended wall beam without notch impact strength		ASTM D256	1300 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ASTM D256	140 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Yield	ASTM D638	60 %
elongation	elongation	Break	ASTM D638	7.0 %
tensile strength	Yield	ASTM D638	110 MPa
Bending modulus		ASTM D790	3590 MPa
bending strength		ASTM D790	162 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ASTM D1525	219 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	207 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	199 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	24hr	ASTM D570	0.25 %
density		ASTM D792	1.27 g/cm³
melt mass-flow rate	337°C/6.6kg	ASTM D1238	18 g/10min
Shrinkage rate	MD	ASTM D955	0.50to0.80 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	0.60to0.90 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale		109

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.