impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot filament ignition temperature	0.71mm	IEC 60695-2-13	960	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	960	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750	°C
UL flame retardant rating	0.40mm	UL 94	V-2
Burning wire flammability index	0.71mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2/1	3000	Mpa
tensile strength	Yield	ISO 527-2/50	84.0	Mpa
Tensile strain	Yield	ISO 527-2	4.4	%
Tensile strain	Tensile strain	Break	ISO 527-2	30	%
Bending modulus		ISO 178	2900	Mpa
bending strength		ISO 178	94.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melting temperature		ISO 11357-3	260	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	TD:2.00mm	ISO 294-4	2.1	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	2.1	%
Water absorption rate	23°C,24hr	ISO 62	1.7	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity	2.00mm	IEC 60093	10	ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	18	KV/mm