PC Makrolon® 2608 Covestro - Polycarbonates

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD	ISO 2577	0.60to0.80 %
	Shrinkage rate	MD	ISO 2577	0.60to0.80 %
		Shrinkage rate	TD:2.00mm3	ISO 294-4	0.70 %
		Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO 294-4	0.65 %
Water absorption rate	饱和,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.12 %
density	23°C	ISO 1183	1.20 g/cm³
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	13 g/10min
Melt volume flow rate	300°C/1.2kg	ISO 1133	12.0 cm³/10min

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
ball-indentation hardness		ISO 2039-1	113 MPa

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
refractive index		ISO 489	1.586
transmissivity	1000µm	ISO 13468-2	89.0 %
	transmissivity	2000µm	ISO 13468-2	89.0 %
		transmissivity	3000µm	ISO 13468-2	88.0 %
		transmissivity	transmissivity	4000µm	ISO 13468-2	87.0 %
Haze ratio	3000µm	ISO 14782	<0.80 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
SelfIgnitionTemperature		ASTM D1929	550 °C
FlashIgnitionTemperature		ASTM D1929	480 °C

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,完全断裂	ISO 7391	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,局部断裂	ISO 7391	65 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6300 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5400 N
Charpy Notched Impact Strength	-30°C,完全断裂	ISO 7391	16 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,局部断裂	ISO 7391	70 kJ/m²

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服,23°C	ISO 527-2/50	65.0 MPa
tensile strength	tensile strength	断裂,23°C	ISO 527-2/50	70.0 MPa
Tensile strain	屈服,23°C	ISO 527-2/50	6.3 %
Tensile strain	Tensile strain	断裂,23°C	ISO 527-2/50	120 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50 %
Tensile creep modulus	1hr	ISO 899-1	2200 MPa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1900 MPa
Flexural modulus	23°C	ISO 178	2350 MPa
bending strength	3.5%Strain,23°C	ISO 178	72.0 MPa
bending strength	bending strength	23°C	ISO 178	96.0 MPa
Bending Strain	23°C	ISO 178	7.0 %
Tensile modulus	23°C	ISO 527-2/1	2350 MPa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	139 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	127 °C
vicat	--	ISO 306/B50	146 °C
vicat	vicat	--	ISO 306/B120	147 °C
ball-indentation hardness	138°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：23到55°C	ISO 11359-2	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
Glass Transition Temperature		ISO 11357-2	148 °C