impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	55	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
bending strength	Yield,50.0mmSpan	ASTM D790	91.0	Mpa
tensile strength	Yield	ISO 527-2/50	58.0	Mpa
	tensile strength	Break	ASTM D638	58.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	52.0	Mpa
elongation	Yield	ASTM D638	4.2	%
Tensile strain	Yield	ISO 527-2/50	4.2	%
elongation	Break	ASTM D638	140	%
Tensile strain	Break	ISO 527-2/50	100	%
Bending modulus	50.0mmSpan	ASTM D790	2900	Mpa
Bending modulus	Bending modulus		ISO 178	2850	Mpa
bending strength		ISO 178	87.0	Mpa
Tensile modulus		ASTM D638	3200	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3000	Mpa
tensile strength	Yield	ASTM D638	57.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	98.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	94.0	°C
Vicat softening temperature		ASTM D152510	130	°C
	Vicat softening temperature	--	ISO 306/B50	132	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	134	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.1E-04	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.1E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	250°C/5.0kg	ASTM D1238	10	g/10min
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	12.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.95-1.1	%
Water absorption rate	Saturation,23°C	ISO 62	0.42	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.14	%