PPS 1140L4 CELANESE USA

ویژگی‌ها:

Injection grade medium melt viscosity

کاربردهای معمول:

During injection molding there is a slight flash

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

کاربردهای معمول:	During injection molding \| there is a slight flash
ویژگی‌ها:	Injection grade \| medium melt viscosity

گواهی‌نامه‌ها

No Data...

برگه داده فنی

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
SpecificHeatCapacity of Melt		Internal Method	1500	J/kg/°C
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	34	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	53	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	53	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Extreme Oxygen Index		ISO 4589-2	47	%
UL flame retardant rating	3.0mm	UL 94	5VA
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.38mm	UL 94	V-0
Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate		ASTM-D570	0.02	%
density		ISO 1183	1.65	g/cm3
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	200°C	ASTM D638	3240	MPa
	Tensile modulus	150°C	ASTM D638	4270	MPa
		Tensile modulus	75°C	ASTM D638	11900	MPa
		Tensile modulus	Tensile modulus	-40°C	ASTM D638	14500	MPa
Rockwell hardness		ASTM-D785	100	R-Scale
Impact strength of cantilever beam gap		ISO 180/1A	10	KJ/m2
Bending modulus		ISO 178	14500	MPa
tensile strength	Break,23°C	ASTM D638	200	MPa
Tensile modulus	--	ISO 527-2/1A/1	14700	MPa
tensile strength	Break	ISO 527-2/1A/5	195	MPa
elongation	Break,23°C	ASTM D638	1.7	%
elongation	elongation	Break	ISO 527-2/1A/5	1.9	%
Bending modulus	23°C	ISO 178	14500	MPa
bending strength		ISO 178	285	MPa
tensile strength		ISO 527	195	MPa
Tensile modulus		ISO 527	14700	MPa
bending strength		ISO 178	285	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Annealed	ASTM D648	280	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	265	°C
		Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	270	°C
		Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	215	°C
Glass transition temperature		ISO 11357-2	90.0	°C
Melting temperature		ISO 11357-3	280	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	4.2E-05	cm/cm/°C
Hot deformation temperature	1.80Mpa	ISO 75-A	270	℃
UL flame retardant rating		UL 94	V-0
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.6E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Saturation,23°C	ISO 62	0.020	%
Shrinkage rate	MD	ISO 294-4	0.20to0.60	%
	Shrinkage rate	TD	ISO 294-4	0.40to0.60	%
		Shrinkage rate	TD	ASTM D955	0.50to0.70	%
		Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.20to0.30	%
Specific volume		ASTM D792	0.611	cm³/g
density		ASTMD792	1.65	g/cm³
Shrinkage rate		ISO 294-4	0.2-0.6	%
Biochemical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Filling amount			40	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index		IEC 60112	PLC 4
Arc resistance		ASTM D495	134	sec
Dissipation factor	1MHz	IEC 60250	6.2E-03
Dielectric constant	1kHz	ASTM D150	3.50
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity	--	ASTM D257	1E+16	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	28	kV/mm
Dielectric constant	1MHz	ASTM D150	3.50
Dielectric constant	Dielectric constant	1MHz	IEC 60250	4.60
Dissipation factor	1kHz	ASTM D150	1E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	1E-03
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	M-Sale	ISO 2039-2	100
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	100
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate		Internal Method	3.18	mm

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.

Supplier Join

تماس با ما

دریافت اپلیکیشن

Top

PPS 1140L4 CELANESE USA

توصیف محصول

گواهی‌نامه‌ها

برگه داده فنی

منبع‌یابی در PLAS.COM

فروش و تأیید صلاحیت

کاوش مواد

نمایه قیمت