برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.51 g/cm³ |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.1 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.50 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.2 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flammability level | | UL 94 | HB |
| Flammability level | | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | -- | ISO 527-2 | 13000 Mpa |
| Tensile modulus | 120°C | ISO 527-2 | 6900 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 6100 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 5700 Mpa |
| Tensile modulus | 200°C | ISO 527-2 | 5300 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 230 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 130 Mpa |
| tensile strength | 断裂, 160°C | ISO 527-2 | 115 Mpa |
| tensile strength | 断裂, 180°C | ISO 527-2 | 105 Mpa |
| tensile strength | 断裂, 200°C | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 6.5 % |
| Tensile strain | 断裂, 160°C | ISO 527-2 | 6.5 % |
| Tensile strain | 断裂, 180°C | ISO 527-2 | 6.5 % |
| Tensile strain | 断裂, 200°C | ISO 527-2 | 6.5 % |
| Flexural modulus | -- | ISO 178 | 11500 Mpa |
| Flexural modulus | 120°C | ISO 178 | 5800 Mpa |
| Flexural modulus | 160°C | ISO 178 | 5200 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 95 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| relative permittivity | 100 Hz | IEC 60250 | 4.30 |
| relative permittivity | 1 MHz | IEC 60250 | 4.00 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 290 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 290 °C |
| melting temperature | | ISO 11357-3 | 295 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 5.0E-5 cm/cm/°C |
| RTI Elec | 0.75 mm | UL 746 | 65.0 °C |
| Thermal Index - 5000 hr | | IEC 60216 | 177 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.