برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| spiral flow length | | 内部方法 | 20.0 cm |
| Shrinkage rate | TD | ISO 294-4 | 1.2 % |
| Shrinkage rate | MD | ISO 294-4 | 1.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60 % |
| Water absorption rate | 100°C，饱和 | ISO 62 | 0.75 % |
| MeltViscosity | 400°C | ISO 11443 | 200 Pa·s |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 86 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | --11 | ISO 4589-2 | 24 % |
| Limiting Oxygen Index | --12 | ISO 4589-2 | 35 % |
| toxicity | COContent | NES713 | 0.0740 |
| toxicity | CO2Content | NES713 | 0.150 |
| toxicity | TotalGases | NES713 | 0.220 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2 | 4300 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 115 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 25 % |
| bending strength | 23°C6 | ISO 178 | 180 MPa |
| bending strength | 125°C | ISO 178 | 105 MPa |
| bending strength | 175°C | ISO 178 | 32.0 MPa |
| bending strength | 275°C | ISO 178 | 16.0 MPa |
| compression stress | 23°C | ISO 604 | 140 MPa |
| compression stress | 120°C | ISO 604 | 90.0 MPa |
| compression stress | 200°C | ISO 604 | 30.0 MPa |
| Flexural modulus | 23°C | ISO 178 | 4000 MPa |
| bending strength | 3.5%Strain,23°C | ISO 178 | 130 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 5.5 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.8 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Volume resistivity | 125°C | IEC 60093 | 1E+15 ohms·cm |
| Volume resistivity | 275°C | IEC 60093 | 1E+09 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 23 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：<152°C | ISO 11359-2 | 4.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | MD：>152°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：<152°C | ISO 11359-2 | 5.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：>152°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| thermal conductivity | 23°C9 | ISO 22007-4 | 0.29 W/m/K |
| thermal conductivity | 23°C10 | ISO 22007-4 | 0.32 W/m/K |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 163 °C |
| Glass Transition Temperature | --7 | ISO 11357-2 | 152 °C |
| Glass Transition Temperature | --8 | ISO 11357-2 | 160 °C |
| melting temperature | | ISO 11357-3 | 373 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.