mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Fracture stress		ISO 527	168	Mpa
Fracture strain		ISO 527	3	%
Tensile modulus		ISO 527	9500	Mpa
Bending modulus		ISO 178	8200	Mpa
Charpy Notched Impact Strength	-40 ℃	ISO 179/1eA	12	kJ/m²
	Charpy Notched Impact Strength	-30℃	ISO 179/1eA	11	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23 ℃	ISO 179/1eA	13	kJ/m²
Impact strength of simply supported beam without notch	-30℃	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23 ℃	ISO 179/1eU	80	kJ/m²
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	Parallel	ISO 11359-1/-2	0.26	E-4/C
Hot deformation temperature	0.45MPa	ASTM D790/ISO 178	216	°C
Hot deformation temperature	Hot deformation temperature	1.80MPa	ASTM D790/ISO 178	200	°C
Melting temperature	10°C/min	ISO 11357-1/-3	218	°C
Linear coefficient of thermal expansion	Normal	ISO 11359-1/-2	0.83	E-4/C
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		IEC 60093	1E+13	E-4/C
Compared to the anti leakage trace index	3.0mm	UL 746A	PLC 1
UL flame retardant rating	0.75mm	UL 94	HB

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.