| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D471 | 1.17 g/cm³ |
| density | | ISO 2781 | 1.17 g/cm³ |
| MeltViscosity | 190°C,300sec^-1 | ASTM D3835 | 370 Pa·s |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| DurometerHardness | ShoreA,1.90mm,CompressionMolded | ASTM D2240 | 57 |
| Shore hardness | ShoreA,1.90mm,CompressionMolded | ISO 868 | 57 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 1.00 mg |
| Torsion Module | -20°C,1.90mm | ASTM D1043 | 6.80 MPa |
| Torsion Module | 24°C,1.90mm | ASTM D1043 | 1.70 MPa |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 100%Strain,125°C,1.90mm4 | ISO 188 | 2.70 MPa |
| elongation | Break,1.90mm2 | ASTM D412 | 390 % |
| elongation | Break,1.90mm2 | ISO 37 | 390 % |
| elongation | Break,125°C,1.90mm4 | ISO 188 | 460 % |
| tear strength | 1.90mm | ASTM D624 | 33.3 kN/m |
| Stretch permanent deformation | | ASTM D412 | 7 % |
| tensile strength | 100%Strain,1.90mm2 | ASTM D412 | 2.90 MPa |
| tensile strength | 100%Strain,125°C,1.90mm4 | ASTM D573 | 2.70 MPa |
| compression set | 24°C,22hr | ASTM D395B | 16 % |
| compression set | 100°C,22hr | ASTM D395B | 72 % |
| compression set | 24°C,22hr | ISO 815 | 16 % |
| compression set | 100°C,22hr | ISO 815 | 72 % |
| Clash Mountain Module | -35°C | ASTM D1043 | 68.9 MPa |
| tensile strength | 100%Strain,1.90mm2 | ISO 37 | 2.90 MPa |
| tensile strength | Yield,1.90mm2 | ASTM D412 | 7.70 MPa |
| tensile strength | Yield,125°C,1.90mm4 | ASTM D573 | 8.30 MPa |
| tensile strength | Yield,1.90mm2 | ISO 37 | 7.70 MPa |
| tensile strength | Yield,125°C,1.90mm4 | ISO 188 | 8.30 MPa |
| elongation | Break,125°C,1.90mm4 | ASTM D573 | 460 % |
| aging | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hardness change rate in the air | ShoreA,125°C,168hr | ASTM D573 | -2.0 |
| volume change | 100°C,168hr,在水中 | ASTM D471 | 10 % |
| volume change | 27°C,168hr,inReferenceFuelB | ISO 1817 | 11 % |
| volume change | 100°C,168hr,inASTM#1Oil | ISO 1817 | -19 % |
| volume change | 100°C,168hr,inIRM903Oil | ISO 1817 | 12 % |
| volume change | 100°C,168hr,在水中 | ISO 1817 | 10 % |
| Shore hardness | ShoreA,125°C,168hr | ISO 188 | -2.0 |
| volume change | 27°C,168hr,inReferenceFuelB | ASTM D471 | 11 % |
| volume change | 100°C,168hr,inASTM#1Oil | ASTM D471 | -19 % |
| volume change | 100°C,168hr,inIRM903Oil | ASTM D471 | 12 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| brittle temperature | | ISO 812 | -74.0 °C |
| brittle temperature | | ASTM D746 | -74.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.