PC Lupoy® 1201-08

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
Water absorption rate	23°C,24hr	ASTM D570	0.15 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ASTM D570	0.32 %
melt mass-flow rate	300°C/1.2kg	ASTM D1238	8.0 g/10min
Shrinkage rate	MD	ASTM D955	0.50to0.70 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M计秤	ASTM D785	73
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	روش آزمون	نتیجه آزمون
refractive index	ASTM D542	1.586
transmissivity	ASTM D1003	89.0 %
Haze ratio	ASTM D1003	0.70to1.5 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	850 °C
Limiting Oxygen Index		ASTM D2863	26 %
Average degree of combustion		ASTM D635	3 cm
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	0.50mm	UL 94	V-2
		UL flame retardant rating	1.6mm	UL 94	V-2
			UL flame retardant rating	2.5mm	UL 94	V-2
			UL flame retardant rating	UL flame retardant rating	2.7mm	UL 94	V-2

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Flexural modulus		ASTM D790	2410 MPa
bending strength		ASTM D790	96.0 MPa
wear resistance	雾度变化	ASTM D1004	45 %
tensile strength	Break	ASTM D638	72.0 MPa
elongation	Yield	ASTM D638	6.0 %
elongation	elongation	Break	ASTM D638	150 %
Tensile modulus		ASTM D638	2410 MPa
tensile strength	屈服,23°C	ASTM D638	60.0 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	900 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	NoBreak
Dart impact	23°C,3.20mm,TotalEnergy	ASTM D3763	89.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dissipation Factor	60Hz	ASTM D150	1E-03
Compared to the Leakage Tracking Index (CTI)	2.00mm	IEC 60112	PLC 2
Volume resistivity	23°C	ASTM D257	2E+17 ohms·cm
dielectric strength		ASTM D149	17 kV/mm
dielectric constant	60Hz	ASTM D150	3.00

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,Annealed,4.00mm，HDT	ASTM D648	144 °C
	Heat distortion temperature	1.8MPa,Unannealed,4.00mm，HDT	ASTM D648	128 °C
	Heat distortion temperature	Heat distortion temperature	1.8MPa,Annealed,4.00mm，HDT	ASTM D648	141 °C
vicat		ASTM D15256	150 °C
Ball pressure temperature		IEC 60598-1	>125 °C
Linear coefficient of thermal expansion	MD：-40到82°C	ASTM D696	6.8E-05 cm/cm/°C