Ethylene Copolymer Tritheva® TN 2007 Brazil Petroquimica
0
- ویژگی‌ها:film
- کاربردها:Laminatesagricultural applicationsfilmsfood packaging
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Secant modulus | 5%正割,MD:50µm,吹塑薄膜 | ASTM D882 | 62.0 MPa |
| 5%正割,TD:50µm,吹塑薄膜 | ASTM D882 | 61.0 MPa | |
| tensile strength | MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 29.0 MPa |
| TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 25.0 MPa | |
| elongation | MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 350 % |
| TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 730 % | |
| melting temperature | 99.0 °C | ||
| gloss | 45°,50.0µm,吹塑薄膜 | ASTM D2457 | 82 |
| 60°,50.0µm,吹塑薄膜 | ASTM D2457 | 130 | |
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | 2.3 % |
| density | ASTM D1505 | 0.933 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.65 g/10min |
| Vinyl acetate content | 9.0to11.0 wt% | ||
| tensile strength | 屈服,模压成型 | ASTM D638 | 6.00 MPa |
| 断裂,模压成型 | ASTM D638 | 22.0 MPa | |
| elongation | 断裂,模压成型 | ASTM D638 | 720 % |