برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
refractive index | | ASTM D-542 | 1.49 |
transmittance | 2mm | ASTM D-1003 | 93 % |
processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Shrinkage rate | | ASTM D-955 | 0.2-0.5 % |
Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Water absorption rate | 24hr | ASTM D-570 | 0.3 % |
melt mass-flow rate | 230℃,37.3n | ASTM D-1238 | 6.0 g/10min |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
tensile strength | | ASTM D-638 | 69[700] MPa[KG/cm |
Impact strength of cantilever beam gap | 1/4槽口副 | ASTM D-256 | 16[1.6] J/m[kg.cm/cm] |
bending strength | 1/4"棒 | ASTM D-790 | 103[1050] MPa[KG/cm |
Flexural modulus | 1/4"棒 | ASTM D-790 | 3.0[3.1×10 GPa[KG/cm |
Rockwell hardness | | ASTM D-785 | 92 M Scale |
elongation | | ASTM D-638 | 7 % |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Volume resistivity | | JIS K-6911 | >10 m[cm] |
Volume resistivity | | JIS K-6911 | >10 |
arc resistance | | JIS K-6911 | 没有痕迹 |
dielectric strength | | | 20[20] MV/m[KV/mm] |
Dielectric loss | 60Hz,正切 | | 0.05 |
dielectric constant | 60Hz | | 3.7 |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
specific heat | | JIS K-7123 | 1.5[0.35] J/g.c[(cal/g/℃)] |
Heat distortion temperature | 1.82MPa,HDT | ASTM D-648 | 89 °C |
Linear coefficient of thermal expansion | | ASTM D-177 | 0.2 W/m℃ |
spiral flow length | 230℃ | MRC | 190-290 mm |
Linear coefficient of thermal expansion | | ASTM D-696 | 6×10 1/℃ |
vicat | 9.8N | ASTM D-1525 | 104 °C |