برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.90 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45°,50.8µm | ASTM D2457 | 56 |
| Haze ratio | 50.8µm | ASTM D1003 | 14 % |
| gloss | 45°，50.8um | ASTM D-2457 | 56 |
| Haze ratio | 50.8um | ASTM D-1003 | 14 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| film thickness | | | 50.8 um |
| density | | ASTM D-792 | 0.921 g/m3 |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 0.9 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Secant modulus | 2% Secant，50.8um，MD | ASTM D-882 | 168 Mpa |
| Secant modulus | 2% Secant，50.8um，TD | ASTM D-882 | 238 Mpa |
| tensile strength | 50.8um，屈服,TD | ASTM D-882 | 14.6 Mpa |
| tensile strength | 50.8um，屈服,MD | ASTM D-882 | 14.2 Mpa |
| tensile strength | 50.8um，TD,断裂 | ASTM D-882 | 39.2 Mpa |
| tensile strength | 50.8um，MD,断裂 | ASTM D-882 | 48.8 Mpa |
| Dart impact | 50.8um | ASTM D-1709A | 300 g |
| Elmendorf tear strength | 50.8um，MD | ASTM D-1922 | 720 g |
| Elmendorf tear strength | 50.8um，TD | ASTM D-1922 | 1000 g |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Thin film puncture strength | 50.8um | 内部方法 | 6.62 J/cm³ |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 1000 g |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 168 Mpa |
| Secant modulus | 2%正割,TD:51µm | ASTM D882 | 238 Mpa |
| tensile strength | MD:屈服,51µm | ASTM D882 | 14.2 Mpa |
| tensile strength | TD:屈服,51µm | ASTM D882 | 14.6 Mpa |
| tensile strength | MD:断裂,51µm | ASTM D882 | 48.8 Mpa |
| tensile strength | TD:断裂,51µm | ASTM D882 | 39.2 Mpa |
| elongation | MD:断裂,51µm | ASTM D882 | 660 % |
| elongation | TD:断裂,51µm | ASTM D882 | 740 % |
| Dart impact | 51µm | ASTM D1709A | 300 g |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 720 g |
| film thickness | | | 51 µm |
| Thin film puncture strength | 51µm | 内部方法 | 6.62 J/cm³ |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D1525 | 107 °C |
| melting temperature | | 内部方法 | 120 °C |
| vicat | | ASTM D-1525 | 107 °C |
| melting temperature | | 内部方法 | 120 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.