برگه داده فنی
| thermosetting | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Thermosetting components | 部件A | | 按重量计算的混合比:120 |
| Thermosetting components | 按重量计算的混合比 | | 100 |
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 0.479 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D,6.35mm | ASTM D2240 | 54 |
| Shore hardness | 邵氏D,12.7mm | ASTM D2240 | 60 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 12.7mm | ASTM D790 | 20.7 MPa |
| compressive strength | 6.35mm | ASTM D695 | 19.3 MPa |
| compressive strength | 12.7mm | ASTM D695 | 13.8 MPa |
| tensile strength | 断裂,6.35mm | ASTM D638 | 9.65 MPa |
| tensile strength | 断裂,12.7mm | ASTM D638 | 11.0 MPa |
| elongation | 断裂,6.35mm | ASTM D638 | 5.0 % |
| elongation | 断裂,12.7mm | ASTM D638 | 5.0 % |
| Flexural modulus | 6.35mm | ASTM D790 | 1170 MPa |
| Flexural modulus | 12.7mm | ASTM D790 | 793 MPa |
| bending strength | 6.35mm | ASTM D790 | 23.4 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | --2 | 内部方法 | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | --3 | 内部方法 | 4.6 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,6.35mm，HDT | ASTM D648 | 80.0 °C |
| Heat distortion temperature | 0.45MPa,未退火,12.7mm，HDT | ASTM D648 | 85.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.