Epoxy Epoxies, Ect. 10-3020 NS Epoxies, Etc.
0
مقایسهبرگه داده فنی
| Uncured Properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| MixRatiobyVolume(PBV) | 固化时间(25°C) | 24to48 hr | |
| 储存稳定性(25°C) | 1000to1500 min | ||
| Color | Clear/Transparent | ||
| MixRatiobyWeight(PBW) | PartA | 1.0 | |
| MixRatiobyVolume(PBV) | 固体含量 | 100 % | |
| 密度(25°C) | 1.15 g/cm³ | ||
| MixRatiobyWeight(PBW) | PartB | 1.0 | |
| MixRatiobyVolume(PBV) | PartA | 1.0 | |
| PartB | 1.0 |
| Cured Properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | ShoreD | 72 | |
| compressive strength | 58.6 MPa | ||
| dielectric strength | 17 kV/mm | ||
| relative permittivity | 1kHz,25°C | 4.00 | |
| Volume resistivity | 25°C | 2E+14 ohms·cm | |
| Dissipation Factor | 1kHz | 0.017 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Operating time | 25°C | 30.0to35.0 min | |
| operate temperature | -50.0-130 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 140 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | 6E-05 cm/cm/°C |