LMDPE ROTOLENE® 93050 Polimeros Mexicanos S.A. de C.V.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 0.935 g/cm³ | |
| Shrinkage rate | ASTM D1895 | 0.33to0.39 | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 5.2 g/10min |
| Environmental stress cracking resistance | 10%Igepal | ASTM D1693 | 300 hr |
| 100%Igepal | ASTM D1693 | >1000 hr | |
| density | ASTM D1505 | 0.321 g/cm³ | |
| Shrinkage rate | ASTM D1895 | 0.33to0.39 | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 5.2 g/10min |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| DegradationTemperature | 190to200 °C | ||
| Pourability | ASTM D1895 | 1500.00to2400.00 g/10min | |
| ASTM D1895 | 1500.00to2400.00 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 18.6 MPa |
| elongation | Yield | ASTM D638 | 12 % |
| Flexural modulus | ASTM D790 | 689 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Low temperature impact | 3.18mm | ARM | 200 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 50.0 °C |