XLPE Pexidan® X/T-UV2 USA Saco Polymers
0
- ویژگی‌ها:physical property
مقایسهبرگه داده فنی
| AcidGasEmission-HBr | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Acid gas release | HBr (溴化氢) | CSAC22.2No.0.3Method2 | 3.7 % |
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| density | ASTM D792 | 1.02 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| Degree of crosslinking | ASTM D2765 | 67 % | |
| tensile strength | Yield | UL 1581 | 12.4 MPa |
| 断裂1 | UL 1581 | 13.6 MPa | |
| 断裂2 | UL 1581 | 12.6 MPa | |
| Break | UL 1581 | 16.2 MPa | |
| 断裂3 | UL 1581 | 15.9 MPa | |
| fracture | UL 1581 | 330 % | |
| UL 1581 | 380 % | ||
| Dissipation Factor | 1MHz | ASTM D150 | 1.2E-03 |
| 100MHz | ASTM D150 | 8E-04 | |
| dielectric strength | -- | UL 1581 | 32000 V |
| afterglancingimpact | UL 1581 | 26000 V | |
| Limiting Oxygen Index | 4.00mm | ASTM D2863 | 24 % |
| fracture | UL 1581 | 430 % | |
| WeatherometerAging | Elongationafterexposure6 | UL 1581 | 400 % |
| insulation resistance | 23°C | UL 1581 | 220000 Mohms/1000ft |
| 90°C | UL 1581 | 2000 Mohms/1000ft | |
| after12weeks:90°C | UL 1581 | 2600 Mohms/1000ft | |
| WeatherometerAging | Elongationafterexposure7 | UL 1581 | 380 % |
| Originalelongation | UL 1581 | 430 % | |
| Originaltensilestrength | UL 1581 | 17.2 MPa | |
| Tensilestrengthafterexposure8 | UL 1581 | 17.1 MPa | |
| TensileStrengthafterexposure9 | UL 1581 | 15.2 MPa | |
| brittle temperature | ASTM D746 | <-75.0 °C | |
| deformation | UL 1581 | 1.0 % | |
| CrushingTest | UL 1581 | 612350 g | |
| HotElongation | 150°C | 内部方法 | 40 % |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.