PA66 INVISTA™ T3000HS1L INVISTA CANADA

مقایسه

برگه داده فنی

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ISO 527-2	47.0 Mpa
Tensile strain	Yield	ISO 527-2	4.5 %
Tensile strain	Tensile strain	Break	ISO 527-2	50 %
Bending modulus		ISO 178	1900 Mpa
Charpy Notched Impact Strength	-40℃	ISO 179	19 kJ/m²
	Charpy Notched Impact Strength	23℃	ISO 179	82 kJ/m²
		Charpy Notched Impact Strength	-30℃	ISO 179	无断裂
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	无断裂
Impact strength of cantilever beam gap	-30℃	ISO 180	17 kJ/m²

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	Across Flow: 23 to 55℃, 2.00 mm	ISO 11359-2	0.00012 cm/cm/℃
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	148 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	61.0 °C
Melting temperature		ISO 11357-3	262 °C
Linear coefficient of thermal expansion	Flow: 23 to 55℃, 2.00 mm	ISO 11359-2	0.00014 cm/cm/℃

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD: 2.00 mm	ISO 294-4	1.6-1.9 %
Shrinkage rate	Shrinkage rate	MD: 2.00 mm	ISO 294-4	1.7-2.0 %