| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Apparent density | | ISO 60 | 0.66 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 13 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 12.0 cm³/10min |
| Shrinkage rate | TD | ISO 2577 | 0.60to0.80 % |
| Shrinkage rate | MD | ISO 2577 | 0.60to0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.12 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| FlashIgnitionTemperature | | ASTM D1929 | 480 °C |
| SelfIgnitionTemperature | | ASTM D1929 | 550 °C |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 5300 N |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C,完全断裂 | ISO 7391 | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,局部断裂 | ISO 7391 | 65 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 60.0 J |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂,23°C | ISO 527-2/50 | 75.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 6.1 % |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 130 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 MPa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 67.0 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 133 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 121 °C |
| vicat | | ISO 306/B50 | 143 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.