PPO(PPE)+PS+PP NORYL PPX™ PPX830 resin SABIC

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	36 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	39 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	95 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	650 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	15.0 J
Dart impact	Dart impact	-30°C,TotalEnergy	ASTM D3763	10.0 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	42 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	42 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Burning wire flammability index	3.0mm	IEC 60695-2-12	650 °C
UL flame retardant rating	1.0mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ISO 527-2/5	98.0 MPa
	tensile strength	Break	ASTM D638	101 MPa
	tensile strength	tensile strength	Break	ISO 527-2/5	98.0 MPa
elongation	Yield	ASTM D638	2.9 %
Tensile strain	Yield	ISO 527-2/5	3.2 %
elongation	Break	ASTM D638	100 %
Tensile strain	Break	ISO 527-2/5	3.2 %
Bending modulus	50.0mmSpan	ASTM D790	6600 MPa
Bending modulus	Bending modulus		ISO 178	7100 MPa
bending strength		ISO 178	141 MPa
Tensile modulus		ISO 527-2/1	7700 MPa
tensile strength	Yield	ASTM D638	101 MPa
bending strength	Yield,50.0mmSpan	ASTM D790	144 MPa
Tensile modulus		ASTM D638	7600 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ISO 306/B120	150 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	2.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-30to80°C	ISO 11359-2	2.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to95°C	ASTME831	1.3E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to80°C	ISO 11359-2	1.2E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	153 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	156 °C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	168 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	166 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.19 g/cm³
Shrinkage rate	TD：3.20mm	Internal Method	0.40to0.60 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.20to0.25 %
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	6.00 cm³/10min
melt mass-flow rate	280°C/5.0kg	ASTM D1238	6.0 g/10min
density		ISO 1183	1.19 g/cm³