PC LEXAN™ 203R-111 SABIC INNOVATIVE NETHERLANDS

ویژگی‌ها:
عقب نشینی
کاربردها:
تجهیزات تناسب اندامروشنایی
مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Refractive index		ASTM D542	1.586
transmissivity	2540 μm	ASTM D1003	88.0 %
turbidity	2540 μm	ASTM D1003	1.0 %

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m
Dart impact	23°C	ASTM D3029	169 J
Impact strength of cantilever beam gap		ASTM D1822	546 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.75 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	6.0 mm	UL 94	V-0

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D638	62.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	65.0 Mpa
elongation	Yield	ASTM D638	7.0 %
elongation	elongation	Break	ASTM D638	110 %
Bending modulus	50.0 mm Span	ASTM D790	2340 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	93.0 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0 mg

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			290 to 310 °C
Temperature in the middle of the barrel			300 to 320 °C
Temperature at the front of the material cylinder			310 to 330 °C
Spray nozzle temperature			305 to 325 °C
Processing (melt) temperature			310 to 330 °C
Mold temperature			80 to 115 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132 °C
Vicat softening temperature		ASTM D15255	154 °C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5 cm/cm/°C
specific heat		ASTM C351	1260 J/kg/°C
thermal conductivity		ASTM C177	0.29 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	130 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Specific volume		ASTM D792	0.830 cm³/g
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	7.0 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.15 %
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35 %
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58 %
Outdoor applicability		UL 746C	f1

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	> 1.0E+17 ohms·cm
Dielectric strength	3.20 mm, in Air	ASTM D149	15 KV/mm
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.96
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.010
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 4

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118