impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	20	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	65	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	60	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.6mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	22	%
UL flame retardant rating	3.2mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Bending strain	23°C	ISO 178/A	5.5	%
bending strength	23°C4	ISO 178/A	135	MPa
bending strength	bending strength	3.5%Strain,23°C	ISO 178/A	125	MPa
Bending modulus	23°C	ISO 178/A	4200	MPa
tensile strength	Break,23°C	ISO 527-2/5	85.0	MPa
Tensile modulus	23°C	ISO 527-2/1	4500	MPa
Tensile strain	Break,23°C	ISO 527-2/5	4.5	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.7E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05	cm/cm/°C
Melting temperature		ISO 11357-3	214	°C
Vicat softening temperature		ISO 306/B120	200	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	175	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	205	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	7.0	%
Shrinkage rate	MD:120°C,4hr,3.00mm3	ISO 2577	0.050	%
	Shrinkage rate	MD:280°C,3.00mm2	ISO 2577	0.30	%
		Shrinkage rate	TD:120°C,4hr,3.00mm3	ISO 2577	0.15	%
		Shrinkage rate	Shrinkage rate	TD:280°C,3.00mm2	ISO 2577	0.83	%
Apparent density		ISO 60	0.60	g/cm³
density	23°C	ISO 1183	1.18	g/cm³
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
ISO Shortcut		ISO 1874	PA6/66-HI.GHR.14-040.GF15