برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.14 g/cm³ |
| density | | ISO 11832 | 1130 kg/m³ |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 5.3 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 18.0 cm³/10min |
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTM D955 | 0.50to0.80 % |
| Water absorption rate | Saturation | ISO 622 | 0.15 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 114 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Nominal fracture strain | | ISO 527-22 | >50 % |
| Flexural modulus | 3.20mm,InjectionMolded | ASTM D790 | 2110 MPa |
| bending strength | 3.20mm | ASTM D790 | 77.5 MPa |
| Tensile modulus | | ISO 527-22 | 2200 MPa |
| tensile strength | 屈服,3.20mm,注塑 | ASTM D638 | 56.9 MPa |
| tensile strength | Yield | ISO 527-22 | 60.0 MPa |
| Tensile strain | Yield | ISO 527-22 | 4.9 % |
| Tensile strain | Break,3.20mm,InjectionMolded | ASTM D638 | >100 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 36.3 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU2 | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| Impact strength of cantilever beam gap | -30°C,3.20mm,注塑 | ASTM D256 | 490 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
| Impact strength of cantilever beam gap | 23°C,3.20mm,注塑 | ASTM D256 | 640 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 600932 | 3.8E+14 ohms |
| Volume resistivity | | IEC 600932 | >1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-12 | 42 kV/mm |
| relative permittivity | 1MHz | IEC 602502 | 2.80 |
| Dissipation Factor | 1MHz | IEC 602502 | 0.010 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 601122 | PLC 3 |
| High arc combustion index (HAI) | 1.6mm | UL 746 | PLC 1 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | |
| Hot wire ignition (HWI) | 1.6mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Imp | 1.6mm | UL 746 | 60.0 °C |
| RTI Imp | 3.0mm | UL 746 | 60.0 °C |
| RTI Str | 1.6mm | UL 746 | 60.0 °C |
| RTI Str | 3.0mm | UL 746 | 60.0 °C |
| Heat distortion temperature | 1.8MPa,Unannealed,6.40mm,InjectionMolded，HDT | ASTM D648 | 113 °C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 104 °C |
| Glass Transition Temperature | | ISO 11357-22 | 150 °C |
| vicat | 50N | ISO 3062 | 119 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 7.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-22 | 8.3E-05 cm/cm/°C |
| RTI Elec | 1.6mm | UL 746 | 60.0 °C |
| RTI Elec | 3.0mm | UL 746 | 60.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.