physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.29 g/cm³
melt mass-flow rate	400°C/2.16kg	ASTM D1238	25 g/10min
Shrinkage rate	MD:3.18mm	ASTM D955	0.70to0.90 %
Shrinkage rate	Shrinkage rate	TD:3.18mm	ASTM D955	1.0to1.2 %
Water absorption rate	24hr	ASTM D570	0.20 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	M-Scale	ASTM D785	94

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.8mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-0

Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون
melt viscosity	400°C,1000sec^-1	ASTM D3835	240 Pa·s

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	--5	ASTM D638	87.0 MPa
elongation	屈服5	ASTM D638	6.2 %
	elongation	Yield	ISO 527-2/1A/50	5.7 %
		elongation	断裂5	ASTM D638	>40 %
		elongation	elongation	Break	ISO 527-2/1A/50	>40 %
Flexural modulus	--	ASTM D790	3100 MPa
Flexural modulus	Flexural modulus	--	ISO 178	3200 MPa
Tensile modulus	--	ISO 527-2/1A/1	3200 MPa
tensile strength	Yield	ISO 527-2/1A/50	89.0 MPa
shear strength		ASTM D732	78.0 MPa
bending strength	--	ASTM D790	124 MPa
bending strength	bending strength	--	ISO 178	127 MPa
compressive strength		ASTM D695	112 MPa
Tensile modulus	--5	ASTM D638	3000 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	--	ASTM D256	69 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	--	ISO 180	6.6 kJ/m²
Suspended wall beam without notch impact strength		ASTMD256	无断裂

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		ASTM D257	>1.9E+17 ohms
Volume resistivity		ASTM D257	5E+17 ohms·cm
dielectric strength	3.00mm	ASTM D149	16 kV/mm
dielectric constant	60Hz	ASTM D150	3.10
	dielectric constant	1kHz	ASTM D150	3.12
	dielectric constant	dielectric constant	1MHz	ASTM D150	3.10
Dissipation Factor	60Hz	ASTM D150	1E-03
	Dissipation Factor	1kHz	ASTM D150	1E-03
	Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	4E-03

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
thermal conductivity		ASTME1530	0.24 W/m/K
Heat distortion temperature	1.8MPa,退火,3.20mm，HDT	ASTM D648	190 °C
Glass Transition Temperature		ASTM D3418	158 °C
melting temperature		ASTM D3418	345 °C
Linear coefficient of thermal expansion	MD：-50到50°C	ASTME831	4.7E-05 cm/cm/°C
specific heat	50°C	DSC	1310 J/kg/°C
specific heat	specific heat	200°C	DSC	1820 J/kg/°C