برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Apparent density | | ISO 60 | 0.70 g/cm³ |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO 2577 | 0.67 % |
| Shrinkage rate | TD:120°C,2hr,3.00mm3 | ISO 294-4 | 0.21 % |
| Shrinkage rate | MD:280°C,3.00mm2 | ISO 2577 | 0.34 % |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO 2577 | 0.10 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 7.8 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.6 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 190 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| Burning Behavior | | ISO 3795 | passed |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ISO Shortcut | | ISO 1874 | PA6/66.GHR.14-060.GF15 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 20 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 25 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 断裂,23°C | ASTM D638 | 117 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 23°C | ASTM D790 | 5700 Mpa |
| Flexural modulus | 23°C | ISO 178/A | 5700 Mpa |
| bending strength | 23°C | ASTM D790 | 185 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
| bending strength | 23°C | ISO 178 | 185 Mpa |
| bending strength | FlexuralStrainatFlexuralStrength5(23°C) | | 4.0 % |
| Tensile modulus | 23°C | ASTM D638 | 6310 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 6300 Mpa |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Thin film puncture strength | --6 | ISO 6603-2 | 1.50 J |
| Thin film puncture strength | --7 | ISO 6603-2 | 2.00 J |
| Thin film puncture strength | --6 | ISO 6603-2 | 505 N |
| Thin film puncture strength | --7 | ISO 6603-2 | 560 N |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1E+13 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 30 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 4.10 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.70 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 8E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.018 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 180 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 55.0 °C |
| vicat | -- | ISO 306/B50 | 200 °C |
| vicat | -- | ISO 306/B120 | 200 °C |
| melting temperature | | ISO 11357-3 | 218 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.