PEI KMI PEI KM-H00R IEP
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.30 g/cm³ | |
| Shrinkage rate | MD | ASTM D995 | 0.50-0.70 % |
| Water absorption rate | ASTM D570 | 0.25 % | |
| melt mass-flow rate | ℃/Kg | ASTM D1238 | 9.0 g/10min |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 23°C | ASTM D638 | 125 MPa |
| elongation at break | 23°C | ASTM D638 | 13 % |
| bending strength | 23°C | ASTM D790 | 160 MPa |
| Flexural modulus | 23°C | ASTM D790 | 3500 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 65 J/m |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 . |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 Ω.cm | |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| dielectric constant | ASTM D150 | 3.10 | |
| Dissipation Factor | ASTM D150 | 0.015 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa未退火，HDT | ASTM D648 | 208 °C |
| vicat | Melting Temperature | ASTM D3418 | 340 °C |