POM Homopolymer Acetal AH100-15M Chase Plastics Services Inc.
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 15 g/10min |
| Shrinkage rate | MD：24hr,3.20mm | ASTM D955 | 1.8to2.1 % |
| TD：24hr,3.20mm | ASTM D955 | 1.8to2.1 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | 断裂,-40°C | ASTM D638 | 40 % |
| 断裂,23°C | ASTM D638 | 80 % | |
| 断裂,24°C | ASTM D638 | >250 % | |
| Flexural modulus | -40°C | ASTM D790 | 3930 MPa |
| 23°C | ASTM D790 | 3100 MPa | |
| 100°C | ASTM D790 | 827 MPa | |
| tensile strength | 屈服,23°C | ASTM D638 | 68.0 MPa |
| Yield,100°C | ASTM D638 | 28.0 MPa | |
| bending strength | ASTM D790 | 99.3 MPa | |
| Tensile modulus | -40°C | ASTM D638 | 3450 MPa |
| 23°C | ASTM D638 | 3250 MPa | |
| 100°C | ASTM D638 | 703 MPa | |
| tensile strength | 屈服,-40°C | ASTM D638 | 86.2 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 75 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 167 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 102 °C |