PA66 Staramide RF006SXP EUROSTAR FRANCE

ویژگی‌ها:

Filler glass fiber reinforced material 30% filler by weight

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

ویژگی‌ها:

Filler | glass fiber reinforced material | 30% | filler by weight

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	8.0	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0	kJ/m²
		Impact strength of cantilever beam gap	-20°C	ISO 180/1A	9.0	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.75mm	UL 94	HB
Burning rate	3.00mm	FMVSS302	2.0	mm/min
Burning rate	Burning rate	2.00mm	FMVSS302	6.0	mm/min
Extreme Oxygen Index		ISO 4589-2	25	%
UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Break	ISO 527-2/5	3.0	%
tensile strength	Break	ISO 527-2/5	170	MPa
Tensile modulus		ISO 527-2/1	9400	MPa
Bending modulus		ISO 178	9000	MPa
bending strength		ISO 178	260	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
RTI		UL 746	65.0	°C
RTI Imp		UL 746	65.0	°C
RTI Elec		UL 746	65.0	°C
thermal conductivity		ASTME1530	0.33	W/m/K
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	248	°C
Vicat softening temperature	--	ISO 306/B50	260	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	258	°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	7.5E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	4.5	%
Shrinkage rate	MD	Internal Method	0.20to0.40	%
density		ASTM D792	1.37	g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	25.0to50.0	cm³/10min
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Relative permittivity	1MHz	IEC 60250	3.20
	Relative permittivity	60Hz	IEC 60250	3.40
	Relative permittivity	Relative permittivity	50Hz	IEC 60250	3.40
Dielectric strength	3.20mm,in Oil	IEC 60243-1	19	kV/mm
Volume resistivity		ASTM D257	>1.0E+16	ohms·cm
Surface resistivity		IEC 60093	>1.0E+16	ohms
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	0.015
	Dissipation factor	60Hz	IEC 60250	6.8E-03
	Dissipation factor	Dissipation factor	50Hz	IEC 60250	6.8E-03
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	L-Sale	ISO 2039-2	113

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.