| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D-792 | 无水｜1.5 |
| density | | ASTM D-792 | 1.9%水｜- |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 无水｜30 mg/1000次 |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 1.9%水｜- mg/1000次 |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 无水｜0.9 % |
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 1.9%水｜- % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | ASTM D-256 | 1.9%水｜120 kg·cm/cm |
| Flexural modulus | 23℃ | ASTM D-790 | 无水｜122000 kg/cm2 |
| Flexural modulus | 23℃ | ASTM D-790 | 1.9%水｜72000 kg/cm2 |
| Flexural modulus | 80℃ | ASTM D-790 | 无水｜63000 kg/cm2 |
| Flexural modulus | 80℃ | ASTM D-790 | 1.9%水｜45000 kg/cm2 |
| Flexural modulus | -40℃ | ASTM D-790 | 无水｜140000 kg/cm2 |
| Flexural modulus | -40℃ | ASTM D-790 | 1.9%水｜120000 kg/cm2 |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜95 M-标度 |
| Rockwell hardness | 23℃ | ASTM D-785 | 1.9%水｜- M-标度 |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜121 R-标度 |
| elongation at break | 23℃ | ASTM D-638 | 无水｜5 % |
| elongation at break | 23℃ | ASTM D-638 | 1.9%水｜5 % |
| Impact strength of cantilever beam gap | -40℃，无缺口1/8 | ASTM D-256 | 无水｜12.5 kg·cm/cm |
| Impact strength of cantilever beam gap | -40℃，无缺口1/8 | ASTM D-256 | 1.9%水｜15 kg·cm/cm |
| Impact strength of cantilever beam gap | -40℃，无缺口1/8 | ASTM D-256 | 无水｜12.5 kg·cm/cm2 |
| Impact strength of cantilever beam gap | -40℃，无缺口1/8 | ASTM D-256 | 1.9%水｜15 kg·cm/cm2 |
| Impact strength of cantilever beam gap | 23℃，V缺口1/2 | ASTM D-256 | 无水｜15 kg·cm/cm |
| Impact strength of cantilever beam gap | 23℃，V缺口1/2 | ASTM D-256 | 1.9%水｜20 kg·cm/cm |
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | ASTM D-256 | 无水｜98 kg·cm/cm |
| shearing strength | 23℃ | ASTM D-732 | 无水｜940 kg/cm2 |
| shearing strength | 23℃ | ASTM D-732 | 1.9%水｜750 kg/cm2 |
| Rockwell hardness | 23℃ | ASTM D-785 | 1.9%水｜- R-标度 |
| bending strength | 23℃ | ASTM D-790 | 无水｜2900 kg/cm2 |
| bending strength | 23℃ | ASTM D-790 | 1.9%水｜1850 kg/cm2 |
| bending strength | 80℃ | ASTM D-790 | 无水｜16000 kg/cm2 |
| bending strength | 80℃ | ASTM D-790 | 1.9%水｜- kg/cm2 |
| bending strength | -40℃ | ASTM D-790 | 无水｜3300 kg/cm2 |
| bending strength | -40℃ | ASTM D-790 | 1.9%水｜- kg/cm2 |
| tensile strength | 23℃，屈服 | ASTM D-638 | 无水｜2000 kg/cm2 |
| tensile strength | 23℃，屈服 | ASTM D-638 | 1.9%水｜1300 kg/cm2 |
| tensile strength | 80℃，屈服 | ASTM D-638 | 无水｜1200 kg/cm2 |
| tensile strength | 80℃，屈服 | ASTM D-638 | 1.9%水｜- kg/cm2 |
| tensile strength | -40℃，屈服 | ASTM D-638 | 无水｜2900 kg/cm2 |
| tensile strength | -40℃，屈服 | ASTM D-638 | 1.9%水｜- kg/cm2 |
| compressive strength | 23℃ | ASTM D-695 | 无水｜1900 kg/cm2 |
| compressive strength | 23℃ | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | 80℃ | ASTM D-695 | 无水｜1000 kg/cm2 |
| compressive strength | 80℃ | ASTM D-695 | 1.9%水｜- kg/cm2 |
| compressive strength | -40℃ | ASTM D-695 | 无水｜2600 kg/cm2 |
| compressive strength | -40℃ | ASTM D-695 | 1.9%水｜- kg/cm2 |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| filler content | | | 无水｜45 wt% |
| filler content | | | 1.9%水｜- wt% |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 106Hz | ASTM D-150 | 无水｜0.02 |
| Dissipation Factor | 106Hz | ASTM D-150 | 1.9%水｜0.06 |
| dielectric strength | 1/8" | ASTM D-149 | 无水｜19 KV/mm |
| dielectric strength | 1/8" | ASTM D-149 | 1.9%水｜15 KV/mm |
| dielectric constant | 106Hz | ASTM D-150 | 无水｜4.2 |
| dielectric constant | 106Hz | ASTM D-150 | 1.9%水｜4.5 |
| dielectric constant | 103Hz | ASTM D-150 | 无水｜4.9 |
| dielectric constant | 103Hz | ASTM D-150 | 1.9%水｜7.4 |
| Volume resistivity | | ASTM D-257 | 无水｜1015 Ω.cm |
| Volume resistivity | | ASTM D-257 | 1.9%水｜1012 Ω.cm |
| Dissipation Factor | 50Hz | ASTM D-150 | 无水｜0.03 |
| Dissipation Factor | 50Hz | ASTM D-150 | 1.9%水｜0.16 |
| arc resistance | 1/8" | ASTM D-495 | 无水｜104 S |
| arc resistance | 1/8" | ASTM D-495 | 1.9%水｜119 S |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL-94 flame retardant grade | 1/32" | UL 94 | 无水｜HB |
| UL-94 flame retardant grade | 1/32" | UL 94 | 1.9%水｜- |
| Heat distortion temperature | 4.6kg/cm2，HDT | ASTM D-648 | 无水｜225 °C |
| Heat distortion temperature | 4.6kg/cm2，HDT | ASTM D-648 | 1.9%水｜- °C |
| melting temperature | | 差示扫描测热计DSC | 无水｜225 °C |
| specific heat | | | 无水｜0.31 Cal/g·℃ |
| specific heat | | | 1.9%水｜- Cal/g·℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 无水｜2-3 ×10-5cm/cm/℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 1.9%水｜- ×10-5cm/cm/℃ |