mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength		ASTM D638/ISO 527	550	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	116
Bending modulus		ASTM D790/ISO 178	26500	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	830	kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	14	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	8	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	7	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	37	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	HDT	ASTM D648/ISO 75	88	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	94	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	6.9x10^5	mm/mm.℃
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792/ISO 1183	10.5
Shrinkage rate		ASTM D955	0.4-0.6	%
Water absorption rate		ASTM D570/ISO 62	0.3	%