ABS Kaneka MUH LG5053 Kaneka Corporation

کاربردها:
Applications in the automotive electrical and electronic fields
مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
gloss	60°	ASTM D523	20

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	50 J/m
	Impact strength of cantilever beam gap	-30°C,6.40mm	ASTM D256	50 J/m
		Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	90 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	80 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength		ASTM D638	44.0 MPa
bending strength		ASTM D790	72.0 MPa
elongation	Break	ASTM D638	30 %
Bending modulus		ASTM D790	2300 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	120 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110 °C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.05 g/cm³
Shrinkage rate	MD	ASTM D955	0.50to0.80 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	110

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.