PBT Chiao Fu PBT PBT819G20 NAT TAIWAN CHIAO FU
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.49 g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | <0.50 % |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 20 g/10min |
| 250°C/2.16kg | ASTM D1238 | 20 g/10min | |
| Shrinkage rate | MD | ASTM D955 | <0.50 % |
| density | ASTM D792 | 1.49 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 0.8mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | Break | ASTM D638 | <5.0 % |
| Flexural modulus | ASTM D790 | 6470 MPa | |
| bending strength | ASTM D790 | 177 MPa | |
| tensile strength | ASTM D638 | 10.8 MPa | |
| bending strength | ASTM D790 | 177 MPa | |
| elongation | Break | ASTM D638 | <5.0 % |
| Flexural modulus | ASTM D790 | 6470 MPa | |
| tensile strength | ASTM D638 | 10.8 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 59 J/m | |
| ASTM D256 | 59 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 205 °C |
| RTI Elec | UL 746 | 75.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 205 °C |
| RTI | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI Elec | UL 746 | 75.0 °C |