| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 0.905 g/cm³ |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45° | ASTM D2457 | 39 |
| Haze ratio | | ASTM D1003 | 14 % |
| transparency | 20μm | ASTM D1746 | 93 |
| gloss | 20 μm | ASTM D2457 | 48 |
| Haze ratio | | ASTM D1003 | 5 % |
| Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | | ASTM D1238 | 0.8 g/10min |
| density | | ASTM D792 | 0.905 g/cm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Puncture Strength | (20 μm) | 陶氏企业测试 | 22 J/cm |
| tensile strength | 屈服 | ASTM D882 | 9 MPa |
| tensile strength | 20 μm (MD) | ASTM D882 | 53 MPa |
| elongation at break | 20μm (MD) | ASTM D882 | 445 % |
| Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Starting temperature of heat sealing | | 陶氏企业测试 | 88 ℃ |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Elmendorf tear strength | TD | ASTM D1922 | 520 g |
| film thickness | | | 25 µm |
| Thin film puncture strength | | 内部方法 | 4.52 J |
| Thin film puncture strength | | 内部方法 | 48.9 N |
| Thin film puncture strength | | 内部方法 | 24.8 J/cm³ |
| film strength | MD | ASTM D882 | 45.5 J/cm³ |
| film strength | TD | ASTM D882 | 64.5 J/cm³ |
| Secant modulus | 1%正割,MD | ASTM D882 | 98.6 MPa |
| elongation | MD:断裂 | ASTM D882 | 340 % |
| elongation | TD:断裂 | ASTM D882 | 570 % |
| Dart impact | | ASTM D1709B | >1100 g |
| Elmendorf tear strength | MD | ASTM D1922 | 370 g |
| Secant modulus | 2%正割,MD | ASTM D882 | 89.6 MPa |
| Secant modulus | 1%正割,TD | ASTM D882 | 113 MPa |
| Secant modulus | 2%正割,TD | ASTM D882 | 93.8 MPa |
| tensile strength | MD:屈服 | ASTM D882 | 6.21 MPa |
| tensile strength | TD:屈服 | ASTM D882 | 5.86 MPa |
| tensile strength | MD:断裂 | ASTM D882 | 32.4 MPa |
| tensile strength | TD:断裂 | ASTM D882 | 30.0 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D1525 | 83.9 °C |
| melting temperature | | 内部方法 | 123 °C |
| vicat | | ASTM D1525 | 84 ℃ |