elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	50%Strain,3.20mm	ASTM D412	2.10	Mpa
	tensile strength	100%Strain,3.20mm	ASTM D412	3.00	Mpa
		tensile strength	300%Strain,3.20mm	ASTM D412	5.20	Mpa
		tensile strength	tensile strength	Break,3.20mm	ASTM D412	24.7	Mpa
elongation	Break,3.20mm	ASTM D412	730	%
tear strength	3.20mm	ASTM D624	66.5	kN/m
Permanent compression deformation	25°C,22hr	ASTM D395B	25	%
Permanent compression deformation	Permanent compression deformation	70°C,22hr	ASTM D395B	75	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber abraser	1000g,H-22Wheel	ASTM D1044	3.00	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Glass transition temperature		DSC	-69.0	°C
Vicat softening temperature		ASTM D15253	75.6	°C
Linear coefficient of thermal expansion	MD	ASTM D696	1.8E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	224°C/8.7kg	ASTM D1238	11	g/10min
Shrinkage rate	MD	ASTM D955	-0.30-0.80	%
Shrinkage rate	Shrinkage rate	TD	ASTM D955	0.40-0.50	%
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA	ASTM D2240	72

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.