HDPE Marlex® HMN TR-945
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Environmental stress cracking resistance | 100%Igepal,模压成型,F50 | ASTM D1693A | 70.0 hr |
| density | ASTM D1505 | 0.945 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 6.0 g/10min |
| Environmental stress cracking resistance | 10%Igepal,模压成型,F50 | ASTM D1693A | 25.0 hr |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ASTM D2240 | 63 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield,3.17mm,RotationalMolded | ASTM D638 | 20.0 MPa |
| Tensile strain | Break,3.17mm,RotationalMolded | ASTM D638 | 460 % |
| Flexural modulus | 2%Secant:3.17mm,RotationalMolded | ASTM D790 | 740 MPa |
| Tangent:3.17mm,RotationalMolded | ASTM D790 | 910 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| ARM impact | -40°C,3.20mm | 92.0 J | |
| -40°C,6.35mm | 223 J |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D15255 | 118 °C | |
| melting temperature | 130 °C | ||
| Crystallization peak temperature | DSC)12 | ASTM D3418 | 113 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,3.17mm,RotationalMolded，HDT | ASTM D648 | 64.0 °C |
| 1.8MPa,Unannealed,3.17mm,RotationalMolded，HDT | ASTM D648 | 44.0 °C | |
| brittle temperature | ASTM D746A | -75.0 °C |