TPU 2103-90AE
35
مقایسه
مشاهده قیمتهابرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melt mass-flow rate | 224°C/8.7kg | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| TD | ASTM D955 | 0.50-0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 47 |
| 邵氏A | ASTM D2240 | 90 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Flexural modulus | 3.20mm | ASTM D790 | 65.9 Mpa |
| Taber abraser | 1000g,H-22转轮 | ASTM D1044 | 50.0 mg |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 50%应变,3.20mm | ASTM D412 | 6.30 Mpa |
| 100%应变,3.20mm | ASTM D412 | 9.70 Mpa | |
| 300%应变,3.20mm | ASTM D412 | 17.9 Mpa | |
| 断裂,3.20mm | ASTM D412 | 38.2 Mpa | |
| elongation | 断裂,3.20mm | ASTM D412 | 530 % |
| tear strength | 3.20mm | ASTM D624 | 133 kN/m |
| compression set | 25°C,22hr | ASTM D395B | 25 % |
| 70°C,22hr | ASTM D395B | 40 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Glass Transition Temperature | DSC | -34.0 °C | |
| vicat | ASTM D15252 | 90.6 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.6E-04 cm/cm/°C |