برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.42 g/cm³ |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.19 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 1.1 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M级 | ASTM D785 | 114 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.41mm | UL 94 | V-0 |
| UL flame retardant rating | 1.9mm | UL 94 | 5VA |
| Limiting Oxygen Index | | ASTM D2863 | 50 % |
| NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 1.30 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ASTM D638 | 6890 Mpa |
| tensile strength | 断裂 | ASTM D638 | 131 Mpa |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| Flexural modulus | 100mmSpan | ASTM D790 | 6890 Mpa |
| bending strength | Break,100mmSpan | ASTM D790 | 228 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 480 J/m |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 460 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 64 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 7E+16 ohms·cm |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 26 KV/mm |
| dielectric constant | 1kHz | ASTM D150 | 3.50 |
| Dissipation Factor | 1kHz | ASTM D150 | 1.5E-03 |
| Dissipation Factor | 2.45GHz | ASTM D150 | 4.9E-03 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Elec | | UL 746 | 170 °C |
| RTI Imp | | UL 746 | 170 °C |
| RTI Str | | UL 746 | 170 °C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| vicat | | ASTM D15255 | 220 °C |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 2.5E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.