PC/PBT 5720U-BK1066 SABIC INNOVATIVE US

فرم：گرانول | درجه：درجه تزریق

تأمین‌کننده(1)

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	47	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	55	kJ/m²
Dart impact	-40°C, Energy at Peak	ASTM D3763	49.0	J
	Dart impact	-40°C, Total Energy	ASTM D3763	59.0	J
		Dart impact	-30°C, Energy at Peak	ASTM D3763	49.0	J
			Dart impact	-30°C, Total Energy	ASTM D3763	61.0	J
				Dart impact	-20°C, Energy at Peak	ASTM D3763	41.0	J
					Dart impact	-20°C, Total Energy	ASTM D3763	53.0	J
						Dart impact	23°C, Energy at Peak	ASTM D3763	44.0	J
						Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	54.0	J
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	--2	ASTM D638	1830	Mpa
	Tensile modulus	--3	Internal Method	1830	Mpa
		Tensile modulus	--4	ASTM D638	1810	Mpa
		Tensile modulus	Tensile modulus	--	ISO 527-2/1	1790	Mpa
tensile strength	Yield5	ASTM D638	47.0	Mpa
	tensile strength	Yield6	Internal Method	45.0	Mpa
		tensile strength	Yield7	ASTM D638	44.0	Mpa
			tensile strength	Yield	ISO 527-2/5	44.0	Mpa
				tensile strength	Yield	ISO 527-2/50	47.0	Mpa
					tensile strength	Break7	ASTM D638	50.0	Mpa
						tensile strength	Break6	Internal Method	47.0	Mpa
							tensile strength	Break5	ASTM D638	48.0	Mpa
							tensile strength	tensile strength	Break	ISO 527-2/5	43.0	Mpa
elongation	Yield7	ASTM D638	4.6	%
	elongation	Yield6	Internal Method	4.6	%
		elongation	Yield5	ASTM D638	4.0	%
			elongation	Yield	ISO 527-2/5	4.1	%
				elongation	Yield	ISO 527-2/50	4.6	%
					elongation	Break7	ASTM D638	120	%
						elongation	Break6	Internal Method	110	%
							elongation	Break5	ASTM D638	120	%
								elongation	Break	ISO 527-2/5	110	%
								elongation	elongation	Break	ISO 527-2/50	120	%
Bending modulus	50.0 mm Span8	ASTM D790	1660	Mpa
Bending modulus	Bending modulus	--9	ISO 178	1860	Mpa
bending strength	--9,10	ISO 178	71.0	Mpa
	bending strength	Yield, 50.0 mm Span8	ASTM D790	70.0	Mpa
	bending strength	bending strength	Break, 50.0 mm Span8	ASTM D790	69.0	Mpa
injection	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
drying temperature			110	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			50 to 80	%
Temperature at the rear of the barrel			245 to 265	°C
Temperature in the middle of the barrel			250 to 270	°C
Temperature at the front of the material cylinder			255 to 275	°C
Spray nozzle temperature			255 to 270	°C
Processing (melt) temperature			260 to 275	°C
Mold temperature			65 to 90	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			50 to 80	rpm
Exhaust hole depth			0.013 to 0.020	mm
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	108	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	117	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span12	ISO 75-2/Bf	109	°C
			Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	83.0	°C
				Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	95.0	°C
				Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span12	ISO 75-2/Af	87.0	°C
Vicat softening temperature	--	ASTM D152513	119	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	122	°C
Linear coefficient of thermal expansion	Flow : -40 to 95°C	ASTM E831	9.8E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	9.8E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 95°C	ASTM E831	1.0E-4	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	1.0E-4	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Specific volume		ASTM D792	0.850	cm³/g
melt mass-flow rate	250°C/2.16 kg	ASTM D1238	3.8	g/10 min
	melt mass-flow rate	250°C/5.0 kg	ASTM D1238	11	g/10 min
		melt mass-flow rate	265°C/2.16 kg	ASTM D1238	6.0	g/10 min
			melt mass-flow rate	266°C/5.0 kg	ASTM D1238	20	g/10 min
			melt mass-flow rate	melt mass-flow rate	250°C/2.16 kg	ISO 1133	3.0	g/10 min
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	3.00	cm3/10min
	Melt Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	10.0	cm3/10min
		Melt Volume Flow Rate (MVR)	265°C/2.16 kg	ISO 1133	6.00	cm3/10min
		Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	18.0	cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	1.0 - 1.2	%
Water absorption rate	Saturation, 23°C	ISO 62	0.28	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.