برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| balance | | % | 0.70to1.5 |
| saturation | | % | 0.060to0.15 |
| melt mass-flow rate | 275°C/2.16kg | g/10min | 3.6to20 |
| flow | | mm/mm | 38.1E-3-78.7E-3 |
| Melt volume flow rate | 275°C/2.16kg | cm³/10min | 0.01to0.04 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot filament ignition temperature | | °C | 798to904 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.222to0.332 |
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.647to20.893 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 0.975to4.365 |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.026to0.044 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| fracture | | | 151.72to280.69 Mpa |
| yield | | % | 2.0to3.0 |
| fracture | | % | 1.6to2.1 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | 23℃ | ohms·cm | 3.0E+2到2.1E+16 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| dielectric strength | 23℃ | V/mil | 500to840 |
| Surface Resistivity | | ohms | 5.0E+3到6.0E+15 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| horizontal | | mm/mm/°C | 55.9E-5-50.8E-5 |
| flow | | mm/mm/°C | 137.2E-5-25.4E-5 |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه