PC 203-22 Trinseo
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183/A | 1.20 g/cm³ | ||
| ISO 11832 | 1200 kg/m³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 22 g/10min |
| 300°C/1.2kg | ISO 1133 | 22 g/10min | |
| Melt volume flow rate | 300°C/1.2kg | ISO 11332 | 18.0 cm³/10min |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| MD | ISO 294-4 | 0.50to0.70 % | |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| 23°C,24hr | ISO 62 | 0.15 % | |
| 平衡,23°C,50%RH | ASTM D570 | 0.32 % | |
| 平衡,23°C,50%RH | ISO 62 | 0.32 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 72 |
| R-Scale | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Haze ratio | ASTM D1003 | 1.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| ISO 489 | 1.586 | ||
| transmissivity | ASTM D1003 | 89.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning Behav. | 1.60mm,UL | ISO 12102 | HB |
| Burning Behav.atthicknessh | 3.20mm,UL | ISO 12102 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| Limiting Oxygen Index (LOI) | ISO 4589-22 | 26 % | |
| Average degree of combustion | ASTM D635 | 3 cm | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 MPa | |
| ISO 527-2/50 | 2300 MPa | ||
| ISO 527-22 | 2300 MPa | ||
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| bending strength | ASTM D790 | 96.5 MPa | |
| ISO 178 | 97.0 MPa | ||
| Taber abraser | ASTM D1044 | 45 % | |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| Yield | ISO 527-22 | 60.0 MPa | |
| Break | ASTM D638 | 65.5 MPa | |
| Break | ISO 527-2/50 | 66.0 MPa | |
| Tensile strain | Yield | ISO 527-22 | 6.0 % |
| elongation | Break | ASTM D638 | 120 % |
| Tensile strain | Break | ISO 527-2/50 | 120 % |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| Flexural modulus | ASTM D790 | 2410 MPa | |
| ISO 178 | 2400 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 70.0 kJ/m² |
| -30°C | ISO 179/1eA2 | 11.0 kJ/m² | |
| 23°C | ISO 179/1eU2 | NoBreak | |
| -30°C | ISO 179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 750 J/m |
| 23°C | ISO 180/A | 74 kJ/m² | |
| 23°C | ASTM D256 | NoBreak | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| InstrumentedDartImpact | 23°C,TotalEnergy | ASTM D3763 | 72.3 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dissipation Factor | 100Hz | IEC 602502 | 1E-03 |
| 1MHz | IEC 602502 | 2E-03 | |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
| Volume resistivity | ASTM D257 | 2E+17 ohms·cm | |
| IEC 600932 | >1.0E+13 ohms·m | ||
| dielectric strength | ASTM D149 | 17 kV/mm | |
| IEC 60243-1 | 17 kV/mm | ||
| IEC 60243-12 | 17 kV/mm | ||
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| 1MHz | ASTM D150 | 3.00 | |
| relative permittivity | 100Hz | IEC 602502 | 3.00 |
| 1MHz | IEC 602502 | 3.00 | |
| Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
| 1MHz | ASTM D150 | 2E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 139 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 126 °C | |
| 1.8MPa，HDT | ISO 75-22 | 128 °C | |
| vicat | ASTM D15257 | 147 °C | |
| ISO 306/B50 | 147 °C | ||
| 50N | ISO 3062 | 147 °C | |
| Ball pressure temperature | IEC 60335-1 | 125 °C | |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| MD | ISO 11359-22 | 7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 126 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 139 °C | |
| 0.45MPa,退火，HDT | ASTM D648 | 142 °C | |
| 0.45MPa,退火，HDT | ISO 75-2/B | 142 °C | |
| 0.45MPa，HDT | ISO 75-22 | 142 °C |