PEI ProPolymers PEI 2200
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.19 % |
| density | ASTM D792 | 1.42 g/cm³ | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| TD | ASTM D955 | 0.40to0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | M-Scale | 114 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 131 MPa |
| elongation | Break | ASTM D638 | 4.0 % |
| Flexural modulus | ASTM D790 | 6890 MPa | |
| bending strength | ASTM D790 | 228 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 64 J/m | |
| ASTM D256 | 9.00 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D256 | 480 J/m | |
| ASTM D256 | 30.0 kJ/m² |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 210 °C |
| 1.8MPa,未退火，HDT | ASTM D648 | 210 °C | |
| vicat | ASTM D1525 | 221 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.