PA/PP HT RNP43MU04AL
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | TD | ASTM D-955 | 0.8 % |
| density | ASTM D-792 | 1.38 g/cm³ | |
| melt mass-flow rate | 275℃/5.0 kg | ASTM D-1238 | 8.4 g/10 min |
| Shrinkage rate | MD | ASTM D-955 | 0.3 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile strength (yield) | 23℃ | ASTM D-638 | 143 MPa |
| elongation at break | 23℃，断裂 | ASTM D-638 | 7.5 % |
| Flexural modulus | 1% 正割 : 23℃ | ASTM D-790 | 945 MPa |
| 正切 : 23℃ | ASTM D-790 | 986 MPa | |
| bending strength | 23℃，屈服 | ASTM D-790 | 203 MPa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 110 J/m |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D-256 | 710 J/m |
| Dart impact | ASTM D-5420 | 0.520 J |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D-648 | 242 ℃ |
| 0.45 MPa, 未退火，HDT | ASTM D-648 | 257 ℃ |