PP Homopolymer TOTAL Polypropylene PPC 4170 TOTAL
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D1505 | 0.905 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 0.75 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,50.0µm,吹塑薄膜 | ASTM D2457 | 7 |
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | 72 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 770 % |
| Dart impact | 50µm,吹塑薄膜 | ASTM D1709A | 350 g |
| tensile strength | MD:屈服,50µm,吹塑薄膜 | ASTM D882 | 26.0 MPa |
| TD:屈服,50µm,吹塑薄膜 | ASTM D882 | 25.0 MPa | |
| MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 59.0 MPa | |
| TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 38.0 MPa | |
| elongation | MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 750 % |
| Elmendorf tear strength | MD:50µm,吹塑薄膜 | ASTM D1922 | 55 g |
| TD:50µm,吹塑薄膜 | ASTM D1922 | 300 g | |
| OTr | 23°C,0%RH,50µm,吹塑薄膜 | ASTM D3985 | 2100 cm³/m²/24hr |
| Water Vapor Transmission Rate | 38°C,100%RH,50µm,吹塑薄膜 | ASTMF1249 | 7.0 g/m²/24hr |
| film thickness | 50 µm | ||
| Secant modulus | 2%正割,MD:50µm,吹塑薄膜 | ASTM D882 | 690 MPa |
| 2%正割,TD:50µm,吹塑薄膜 | ASTM D882 | 600 MPa |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | DSC | 160to165 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.