mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2	2600	Mpa
tensile strength	Yield,23°C	ISO 527-2	63.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.6	%
bending strength		ISO 178	100	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	124	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	105	°C
Vicat softening temperature	--	ISO 306/A50	134	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	120	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7.0E-5到9.0E-5	cm/cm/°C
thermal conductivity		DIN 52612	0.17	W/m/K
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	10.0	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	25.0	cm3/10min
Shrinkage rate		ISO 294-4	0.50-0.90	%
Water absorption rate	Saturation,23°C	ISO 62	0.60	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.18	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	1E+13	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric constant	100Hz	IEC 60250	3.10
Dissipation factor	100Hz	IEC 60250	6E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.012
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	110	Mpa
film	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
elongation	Break	ISO 527-3	>50	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.