PP GK-17
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.04 g/cm³ | |
| Water absorption rate | Saturation | ASTM D570 | 0.060 % |
| density | ASTM D792 | 1.04 g/cm³ | |
| Water absorption rate | Saturation | ASTM D570 | 0.060 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 29 % | |
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 29 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film thickness | 360to510 µm | ||
| tensile strength | MD:屈服 | ASTM D882 | 30.3 MPa |
| TD:屈服 | ASTM D882 | 22.1 MPa | |
| handle | ASTM D2578 | >50 dyne/cm | |
| film thickness | 360to510 µm | ||
| tensile strength | MD:屈服 | ASTM D882 | 30.3 MPa |
| TD:屈服 | ASTM D882 | 22.1 MPa | |
| handle | ASTM D2578 | >50 dyne/cm |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 4E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 57 kV/mm | |
| dielectric constant | ASTM D150 | 2.30 | |
| Dissipation Factor | ASTM D150 | 1.9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | ASTM D3638 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 sec |
| dielectric strength | ASTM D149 | 24800 V | |
| ASTM D149 | 57 kV/mm | ||
| dielectric constant | ASTM D150 | 2.30 | |
| Dissipation Factor | ASTM D150 | 1.9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | ASTM D3638 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | mm/min |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 4 sec |
| dielectric strength | ASTM D149 | 24800 V | |
| Volume resistivity | ASTM D257 | 4E+15 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 121 °C |
| RTI Elec | UL 746 | 115 °C | |
| RTI | UL 746 | 115 °C | |
| Hot deformation temperature (HDT) | 0.45MPa,未退火，HDT | ASTM D648 | 121 °C |
| RTI Elec | UL 746 | 115 °C | |
| RTI | UL 746 | 115 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.