| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 18 g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.88-0.94 % |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.95-1.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 3.8 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.50 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-1 |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB5VA |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服4 | ASTM D638 | 88.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 88.0 Mpa |
| tensile strength | 断裂4 | ASTM D638 | 88.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 88.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 4600 Mpa |
| Flexural modulus | --6 | ISO 178 | 4600 Mpa |
| bending strength | --6,7 | ISO 178 | 145 Mpa |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 145 Mpa |
| Tensile modulus | --3 | ASTM D638 | 5000 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 5000 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 12.0 J |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 23 KV/mm |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 220 °C |
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Bf | 224 °C |
| vicat | -- | ASTMD152511 | 218 °C |
| vicat | -- | ISO 306/B120 | 220 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 4.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.