برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 20 g/10min |
| Shrinkage rate | MD：2.00mm | ASTM D955 | 1.3 % |
| Water absorption rate | 平衡,23°C,65%RH | ASTM D570 | 0.36 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏D | ASTM D2240 | 57 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D638 | 38.0 Mpa |
| elongation | 断裂 | ASTM D638 | 500 % |
| Flexural modulus | | ASTM D790 | 289 Mpa |
| Compression Modulus | | ASTM D695 | 19.1 Mpa |
| Taber abraser | 1000Cycles | ASTM D1044 | 10.0 mg |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 50%应变 | ASTM D412 | 19.6 Mpa |
| tear strength | | ASTM D624 | 177 kN/m |
| compression set | | ASTM D395 | 60 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 2E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 30 KV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 117 °C |
| brittle temperature | | ASTM D746 | -65.0 °C |
| vicat | | ASTM D1525 | 190 °C |
| melting temperature | | DSC | 212 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.4E-04 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.