برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.1 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 5.7 % |
| Water absorption rate | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.8 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | 1.00 mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| FMVSS combustion rate | | FMVSS 302 | B |
| 雾化 - G-value (condensate) | | ISO 6452 | 6.0E-4 g |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 200 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 9500 Mpa |
| bending strength | | ISO 178 | 280 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Ejection Temperature | | | 210 °C |
| Emission of Organic Compounds | | VDA 277 | 10.0 µgC/g |
| Odor | | VDA 270 | 3.00 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 275 to 295 °C |
| Melt Temperature, Optimum | | | 285 °C |
| Temperature | | | 70 to 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | Drying Recommended | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 261 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 252 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : -40 到 23°C | ISO 11359-2 | 2.4E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : 55 到 160°C | ISO 11359-2 | 1.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 8.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -40 到 23°C | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 55 到 160°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |