impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	23°C,TotalEnergy	ASTM D3763	40.0	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/1A	25	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	25	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2/1	3300	Mpa
tensile strength	Yield	ASTM D638	53.0	Mpa
Tensile modulus		ASTM D638	3300	Mpa
tensile strength	Yield	ISO 527-2/5	55.0	Mpa
	tensile strength	Break	ASTM D638	44.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/5	43.0	Mpa
elongation	Yield	ASTM D638	4.5	%
Tensile strain	Yield	ISO 527-2/5	4.5	%
elongation	Break	ASTM D638	20	%
Tensile strain	Break	ISO 527-2/5	13	%
Bending modulus	50.0mmSpan	ASTM D790	3200	Mpa
Bending modulus	Bending modulus		ISO 178	3300	Mpa
bending strength		ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	95.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature		ASTM D152510	145	°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	134	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	135	°C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.9E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	4.1E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	4.1E-05	cm/cm/°C
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	146	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	144	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.46	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.12	%
Shrinkage rate	MD：3.20mm	Internal Method	0.20-0.60	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	10.3	cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	11	g/10min
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dielectric strength	1.60mm,inOil	ASTM D149	32	KV/mm
Volume resistivity		ASTM D257	1.8E+17	ohms·cm
Surface resistivity		ASTM D257	2.9E+17	ohms
Dielectric constant	1MHz	ASTM D150	3.04
Dielectric constant	Dielectric constant	1.90GHz	Internal Method	2.95
Dissipation factor	1MHz	ASTM D150	8.6E-03
Dissipation factor	Dissipation factor	1.90GHz	Internal Method	5.8E-03

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.