| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Apparent density | | g/cm³ | 0.13to0.56 |
| Environmental stress cracking resistance | 23℃ | hr | 0.317to1000 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 23℃ | | 49to62 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | | % | 68.0to92.3 |
| gloss | | | 30to95 |
| gloss | | | 35to82 |
| transparency | | | 26.9to95.3 |
| Haze ratio | | % | 0.40to21 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Multi axis Instrumented Impact Energy | 23℃ | J | 8.19to34.30 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| fracture | | | 6.97to31.38 Mpa |
| fracture | | % | 47to1000 |
| Flexural modulus | 摩擦系数 | | 0.086to0.52 |
| yield | | % | 2.0to23 |
| yield | | % | 14to22 |
| yield | | | 7.45to21.38 Mpa |
| yield | | | 7.66to17.24 Mpa |
| Flexural modulus | 23℃ | | 260.0to271.03 Mpa |
| fracture | | % | 290to940 |
| yield | | | 175.86to281.38 Mpa |
| fracture | | | 9.45to32.69 Mpa |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| MD | | kg·m/cm³ | 1116.45 |
| Initial sealing temperature | | °C | 99to130 |
| TD | | | 200.0 Mpa |
| TD: Yield | TD，屈服 | | 8.83to13.31 Mpa |
| TD | | kg·m/cm³ | 1182.64 |
| MD: Surrender | | % | 12to530 |
| Thin film puncture strength | | kg·m/cm³ | 78.11 |
| TD: Fracture | | % | 660to920 |
| film thickness | | mil | 0.94to2.1 |
| Thin film puncture strength | | n | 1.5506to3.1685 |
| MD | | | 108.28to230.34 Mpa |
| TD: Fracture | | | 18.97to45.17 Mpa |
| TD: Yield | TD，屈服 | % | 4.0to760 |
| MD: Fracture | | % | 350to910 |
| fracture | | % | 520to920 |
| fracture | | | 24.0to50.0 Mpa |
| MD | | g | 0.0to490 |
| TD | | | 115.86to291.03 Mpa |
| yield | | | 5.2to16.97 Mpa |
| MD: Fracture | | | 30.0to57.38 Mpa |
| Thin film puncture strength | | N.m | 347.79 |
| TD | | g | 8.0to810 |
| MD | | | 179.31 Mpa |
| MD: Surrender | | | 8.0to13.24 Mpa |
| شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tear strength | 23℃ | n/m | 3938.05to9380.53 |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | 23℃ | ohms·cm | 1.0E+5到1.7E+16 |
| dielectric strength | 23℃ | V/mil | 500to760 |
| dielectric constant | 23℃ | | 2.10to2.55 |
| Dissipation Factor | 23℃ | | 1.0E-4到3.0E-3 |